Description
A two-component, aliphatic poly-aspartic topcoat with slow curing, designed for fast-turnaround projects. It offers deep penetration, strong bonding, and long-lasting resistance to abrasion, impact, wear, and color fading.
A two-component, aliphatic poly-aspartic topcoat with slow curing, designed for fast-turnaround projects. It offers deep penetration, strong bonding, and long-lasting resistance to abrasion, impact, wear, and color fading.
More Prducts
More Prducts
More Prducts
More Prducts
3rd layer - Seal Coat – HPMMA 7204
Checking the right the amount of BPO and mix it with HPMMA 7204
Its function is to Seals the surface, protects from moisture, UV and abrasion. Clear or pigmented
Distributed roughly using a serrated rubber blade (serration approx. 1 mm) and then evenly applied with a mohair roller (pile 4 mm) – Layer thickness 400 to max. 800 micron (400 - 800 g/m²).
Can be pigmented with 2–5 % w/w pigment powder
If applied over a broadcasted surface with chips, the surface MUST be well prepared and excess chips are removed and then vacuumed to prevent unevenness and air bubble formation
HPMMA 7204 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – hard – potlife 8-12 min – curing time 20 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 1.5 | 25-30 | 45-50 |
+10 | 1.5 | 15-20 | 35-40 |
+20 | 1.0 | 12-15 | 25-30 |
>25 | 1.0 | 8-12 | 15-20 |
2nd layer - Base/Wear Coat Mortar – HPMMA 7203
Intermediate layer is characterized by their good filling and leveling properties/ self leveling.
Layer thicknesses of 2-4 mm thickness.
The typical filler consumption is approx. 1.9 kg/m² per mm layer thickness.
The self-leveling mixture is distributed using a pin rake.
If required, especially for decorative flooring, Color chips, preferably sized 3–4 mm, can be broadcast over the self
leveling coating before curing
HPMMA 7203 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – flexible–
potlife 20-25min – curing time 60-70 min – mixed with fillers, pigments, or broadcasted with flakes
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 4.5 | APRX. 40 | APRX. 70 |
+10 | 3 | APRX. 35 | APRX. 75 |
+20 | 2 | APRX. 15 | APRX. 35 |
>30 | 1 | APRX. 25 | APRX. 70 |
1st layer - Primer – HPMMA 7202
Checking the right the amount of BPO and mix it with HPMMA 7202
Its function is to Impregnate the upper layer of concrete and closes pores
Apply it on the substrate using a rubber blade and rolled out in an evenly thin layer, Almost 400 -500 micron (400 - 500 g/m²)
Highly absorbent substrates are coated with primer twice.
The primer is broadcast with quartz sand (Ø 0.4 - 0.8 mm). To improve the adhesion between the primer and the coating.
HPMMA 7202 is low viscous (80 - 100 mPa·s @ 23 ºC) – very hard potlife 6.5-7.0 min – curing time 30 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 5 | APRX. 8 | APRX. 30 |
+10 | 4 | APRX. 8 | APRX. 30 |
+15 | 3 | APRX. 7 | APRX. 30 |
+20 | 2 | APRX. 8 | APRX. 30 |
>30 | 1 | APRX. 6.5 | APRX. 30 |
Hard 2K solvent free Polyurethane parquet adhesive – Shore A 40
Flexible 2K solvent free Polyurethane construction sealants – Shore A 17
Solvent Free Epoxy Filler
A two-component High Build Solvent-free Flooring epoxy filler for heavy-duty applications based on polyamine-cured epoxy resin, to level and fill cracks before overcoating.
3rd layer - Seal Coat – HPMMA 7204
Checking the right the amount of BPO and mix it with HPMMA 7204
Its function is to Seals the surface, protects from moisture, UV and abrasion. Clear or pigmented
Distributed roughly using a serrated rubber blade (serration approx. 1 mm) and then evenly applied with a mohair roller (pile 4 mm) – Layer thickness 400 to max. 800 micron (400 - 800 g/m²).
Can be pigmented with 2–5 % w/w pigment powder
If applied over a broadcasted surface with chips, the surface MUST be well prepared and excess chips are removed and then vacuumed to prevent unevenness and air bubble formation
HPMMA 7204 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – hard – potlife 8-12 min – curing time 20 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 1.5 | 25-30 | 45-50 |
+10 | 1.5 | 15-20 | 35-40 |
+20 | 1.0 | 12-15 | 25-30 |
>25 | 1.0 | 8-12 | 15-20 |
2nd layer - Base/Wear Coat Mortar – HPMMA 7203
Intermediate layer is characterized by their good filling and leveling properties/ self leveling.
Layer thicknesses of 2-4 mm thickness.
The typical filler consumption is approx. 1.9 kg/m² per mm layer thickness.
The self-leveling mixture is distributed using a pin rake.
If required, especially for decorative flooring, Color chips, preferably sized 3–4 mm, can be broadcast over the self
leveling coating before curing
HPMMA 7203 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – flexible–
potlife 20-25min – curing time 60-70 min – mixed with fillers, pigments, or broadcasted with flakes
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 4.5 | APRX. 40 | APRX. 70 |
+10 | 3 | APRX. 35 | APRX. 75 |
+20 | 2 | APRX. 15 | APRX. 35 |
>30 | 1 | APRX. 25 | APRX. 70 |
1st layer - Primer – HPMMA 7202
Checking the right the amount of BPO and mix it with HPMMA 7202
Its function is to Impregnate the upper layer of concrete and closes pores
Apply it on the substrate using a rubber blade and rolled out in an evenly thin layer, Almost 400 -500 micron (400 - 500 g/m²)
Highly absorbent substrates are coated with primer twice.
The primer is broadcast with quartz sand (Ø 0.4 - 0.8 mm). To improve the adhesion between the primer and the coating.
HPMMA 7202 is low viscous (80 - 100 mPa·s @ 23 ºC) – very hard potlife 6.5-7.0 min – curing time 30 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 5 | APRX. 8 | APRX. 30 |
+10 | 4 | APRX. 8 | APRX. 30 |
+15 | 3 | APRX. 7 | APRX. 30 |
+20 | 2 | APRX. 8 | APRX. 30 |
>30 | 1 | APRX. 6.5 | APRX. 30 |
Hard 2K solvent free Polyurethane parquet adhesive – Shore A 40
3rd layer - Seal Coat – HPMMA 7204
Checking the right the amount of BPO and mix it with HPMMA 7204
Its function is to Seals the surface, protects from moisture, UV and abrasion. Clear or pigmented
Distributed roughly using a serrated rubber blade (serration approx. 1 mm) and then evenly applied with a mohair roller (pile 4 mm) – Layer thickness 400 to max. 800 micron (400 - 800 g/m²).
Can be pigmented with 2–5 % w/w pigment powder
If applied over a broadcasted surface with chips, the surface MUST be well prepared and excess chips are removed and then vacuumed to prevent unevenness and air bubble formation
HPMMA 7204 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – hard – potlife 8-12 min – curing time 20 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 1.5 | 25-30 | 45-50 |
+10 | 1.5 | 15-20 | 35-40 |
+20 | 1.0 | 12-15 | 25-30 |
>25 | 1.0 | 8-12 | 15-20 |
2nd layer - Base/Wear Coat Mortar – HPMMA 7203
Intermediate layer is characterized by their good filling and leveling properties/ self leveling.
Layer thicknesses of 2-4 mm thickness.
The typical filler consumption is approx. 1.9 kg/m² per mm layer thickness.
The self-leveling mixture is distributed using a pin rake.
If required, especially for decorative flooring, Color chips, preferably sized 3–4 mm, can be broadcast over the self
leveling coating before curing
HPMMA 7203 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – flexible–
potlife 20-25min – curing time 60-70 min – mixed with fillers, pigments, or broadcasted with flakes
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 4.5 | APRX. 40 | APRX. 70 |
+10 | 3 | APRX. 35 | APRX. 75 |
+20 | 2 | APRX. 15 | APRX. 35 |
>30 | 1 | APRX. 25 | APRX. 70 |
1st layer - Primer – HPMMA 7202
Checking the right the amount of BPO and mix it with HPMMA 7202
Its function is to Impregnate the upper layer of concrete and closes pores
Apply it on the substrate using a rubber blade and rolled out in an evenly thin layer, Almost 400 -500 micron (400 - 500 g/m²)
Highly absorbent substrates are coated with primer twice.
The primer is broadcast with quartz sand (Ø 0.4 - 0.8 mm). To improve the adhesion between the primer and the coating.
HPMMA 7202 is low viscous (80 - 100 mPa·s @ 23 ºC) – very hard potlife 6.5-7.0 min – curing time 30 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 5 | APRX. 8 | APRX. 30 |
+10 | 4 | APRX. 8 | APRX. 30 |
+15 | 3 | APRX. 7 | APRX. 30 |
+20 | 2 | APRX. 8 | APRX. 30 |
>30 | 1 | APRX. 6.5 | APRX. 30 |
Hard 2K solvent free Polyurethane parquet adhesive – Shore A 40
Flexible 2K solvent free Polyurethane construction sealants – Shore A 17
Solvent Free Epoxy Filler
A two-component High Build Solvent-free Flooring epoxy filler for heavy-duty applications based on polyamine-cured epoxy resin, to level and fill cracks before overcoating.
Poly-Aspartic Crack Filler
A two-component solvent-free Poly-aspartic crack filler, which provides an advanced solution formulated to effectively fill and repair cracks in various surfaces.
Solvent-Free Epoxy Putty: High-Strength, Zero-VOC Repair Solution
A solvent-free epoxy putty is a two-part, non-toxic repair compound that cures into an ultra-durable, chemical-resistant solid without releasing harmful VOCs (volatile organic compounds). Ideal for industrial, marine, and food-safe applications where fumes or contamination are a concern.
3rd layer - Seal Coat – HPMMA 7204
Checking the right the amount of BPO and mix it with HPMMA 7204
Its function is to Seals the surface, protects from moisture, UV and abrasion. Clear or pigmented
Distributed roughly using a serrated rubber blade (serration approx. 1 mm) and then evenly applied with a mohair roller (pile 4 mm) – Layer thickness 400 to max. 800 micron (400 - 800 g/m²).
Can be pigmented with 2–5 % w/w pigment powder
If applied over a broadcasted surface with chips, the surface MUST be well prepared and excess chips are removed and then vacuumed to prevent unevenness and air bubble formation
HPMMA 7204 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – hard – potlife 8-12 min – curing time 20 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 1.5 | 25-30 | 45-50 |
+10 | 1.5 | 15-20 | 35-40 |
+20 | 1.0 | 12-15 | 25-30 |
>25 | 1.0 | 8-12 | 15-20 |
2nd layer - Base/Wear Coat Mortar – HPMMA 7203
Intermediate layer is characterized by their good filling and leveling properties/ self leveling.
Layer thicknesses of 2-4 mm thickness.
The typical filler consumption is approx. 1.9 kg/m² per mm layer thickness.
The self-leveling mixture is distributed using a pin rake.
If required, especially for decorative flooring, Color chips, preferably sized 3–4 mm, can be broadcast over the self
leveling coating before curing
HPMMA 7203 is intermediate viscous (180 - 200 mPa·s @ 23 ºC) – flexible–
potlife 20-25min – curing time 60-70 min – mixed with fillers, pigments, or broadcasted with flakes
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 4.5 | APRX. 40 | APRX. 70 |
+10 | 3 | APRX. 35 | APRX. 75 |
+20 | 2 | APRX. 15 | APRX. 35 |
>30 | 1 | APRX. 25 | APRX. 70 |
1st layer - Primer – HPMMA 7202
Checking the right the amount of BPO and mix it with HPMMA 7202
Its function is to Impregnate the upper layer of concrete and closes pores
Apply it on the substrate using a rubber blade and rolled out in an evenly thin layer, Almost 400 -500 micron (400 - 500 g/m²)
Highly absorbent substrates are coated with primer twice.
The primer is broadcast with quartz sand (Ø 0.4 - 0.8 mm). To improve the adhesion between the primer and the coating.
HPMMA 7202 is low viscous (80 - 100 mPa·s @ 23 ºC) – very hard potlife 6.5-7.0 min – curing time 30 min
Temperature [°C]*) | Hardener [W/W % ]**) | Potlife [min] | Curing time [min] |
|---|---|---|---|
+5 | 5 | APRX. 8 | APRX. 30 |
+10 | 4 | APRX. 8 | APRX. 30 |
+15 | 3 | APRX. 7 | APRX. 30 |
+20 | 2 | APRX. 8 | APRX. 30 |
>30 | 1 | APRX. 6.5 | APRX. 30 |
Hard 2K solvent free Polyurethane parquet adhesive – Shore A 40